In vitro evaluation of shear bond strength of veneering ceramics to zirconia.
(74/152)
The bond strength between veneering ceramic and zirconia framework is the weakest link in the layered structure. To investigate the shear bond strength (SBS) of veneering ceramics to zirconia, four types of zirconia ceramics (Zirkonzahn, Cercon, Lava, DC-Zirkon) were selected. For each zirconia system, 30 disk specimens were layered with IPS e.max Ceram, Vita VM9, and a manufacturer-recommended veneering ceramic. SBS test was conducted, and fracture surface analysis was also performed to determine the failure modes. One-way ANOVA, two-way ANOVA, and Tukey's HSD tests were used to analyze the data. On shear bond strength between zirconia and their recommended veneering ceramics, statistically significant differences were observed among the different zirconia systems (p<0.001). DC-Zirkon exhibited the highest SBS value (40.49+/-8.43 MPa), followed by Lava (27.11+/-2.72 MPa), Zirkonzahn (24.46+/-3.72 MPa), and Cercon (20.19+/-5.12 MPa). On shear bond strength to IPS e.max Ceram and Vita VM9, significantly lower (p<0.001) were observed for these veneering ceramics than their recommended veneering ceramics for DC-Zirkon and Lava. For Zirkonzahn and Cercon, similar SBS values were observed for all kinds of veneering ceramics (p>0.05). In conclusion, the bonding of manufacturer-recommended veneering ceramic to the zirconia framework differed according to zirconia type. (+info)
Evaluation of Candida albicans formation on feldspathic porcelain subjected to four surface treatment methods.
(75/152)
Candida albicans, known for its adhesion on prosthetic materials and oral tissues, is the most frequently encountered fungal infection in dentistry. The aim of this study was to evaluate the effects of four different surface treatment methods and immersion in artificial saliva on the surface roughness of and candida adhesion on dental porcelains. The four surface treatment methods were namely: natural glaze, overglaze, dual ion exchange, and polishing. Surface roughness of porcelain was evaluated using a surface profilometer and by SEM. Candida adhesion was examined by culturing two Candida strains on porcelain specimens followed by a colorimetric method using XTT/Coenzyme Q0. It became evident that Candida adhesion was found more in the specimens treated with natural glaze and polishing. Further, by the visual inspection of SEM images and comparison of surface roughness, polished and natural-glazed specimens showed rougher surface characteristics than overglazed and dual-ion-exchanged specimens. (+info)
Effects of different food colorants and polishing techniques on color stability of provisional prosthetic materials.
(76/152)
The main objective was to investigate the effects of different polishing techniques on the color stability of provisional prosthetic materials upon exposure to different staining agents by mimicking the oral environment in vitro. Fifty-six cylindrical specimens were prepared for each type of material: bis-acryl and light-polymerized composite resins, and methyl methacrylate- and ethyl methacrylatebased resins. The specimens were polished using seven different polishing techniques and then immersed in four different staining agents. Color was measured with a spectrophotometer before and after immersion, and color changes (DeltaE) were calculated. The effects of the type of provisional material, polishing procedure, staining agent, and their interactions on color stability were significant (p<0.05). Amongst these factors, the staining agent exerted the strongest effect on color stability. Amongst the provisional materials tested, methacrylate-based resins exhibited the highest color stability irrespective of polishing technique and staining agent. (+info)
Effects of metal primers on bonding of adhesive resin cement to noble alloys for porcelain fusing.
(77/152)
This study evaluated the effects of metal primers on the bonding of adhesive resin to four pure metals (Au, Pd, Ag, Cu) and two noble alloys for porcelain fusing (high-gold and high-palladium content alloys). Bonding surface was polished with 600-grit silicon carbide paper and primed with one of the three metal primers (V-Primer, Metaltite, and M.L. Primer). Bonded specimens were fabricated by applying adhesive resin (Super-Bond C&B) on the primed surface. Shear bond strength (SBS) was determined both before and after thermocycling (4-60 degrees C for 2,000 cycles). The highest SBS values to each pure metal after thermocycling were 33.5 MPa for Au by M.L. Primer, 35.0 MPa for Ag by V-Primer, and 34.4 MPa for Cu by Metaltite. SBS to high-gold content alloy after thermocycling was 33.3 MPa by M.L. Primer. None of the primers was effective for pure Pd and high-palladium content alloy after thermocycling. (+info)
Surface texture and roughness of polished nanofill and nanohybrid resin composites.
(78/152)
Nanofiller-containing resin composites have gained appreciable market share in dentistry due to their claims of high mechanical strength and low polymerization contraction. In this study, the polishability of one nanofill (Filtek Supreme XT/FIL) and three nanohybrid materials (Grandio/GRA, Tetric EvoCeram/TET, Venus Diamond/VED) was investigated using surface profilometry and SEM. After the specimens were cured under a Mylar strip or pre-ground with 600-grit SiC paper, three polishing systems were applied and their polishing effects compared: diamond polishing points, a diamond paste, and urethane-backed aluminum oxide disks. Except for the profilometry results obtained by glass filler-containing GRA and VED with one polishing system that comprised the consecutive application of diamond particles and a diamond polishing paste, the final roughness (Ra) of all other specimens were lower than the clinically acceptable 0.2 microm threshold. The surface textures of the polished nanofill FIL and nanohybrid TET were uniformly smooth, whereas relief polishing effects and filler extrusion of varying extents were seen on the nanohybrid composites GRA and VED. (+info)
Effects of different polishing techniques on the surface roughness of dental porcelains.
(79/152)